Tungsten and rhenium made of various components of tungsten-rhenium alloy, these alloys overcome the shortcomings of pure tungsten and pure rhenium, with many excellent properties, such as high melting point, high strength, high hardness, high plasticity, high recrystallization temperature, high thermoelectric potential value, low steam pressure, low electron escape work and low plastic-brittle transition temperature, colleagues they also have excellent Odpornost na reakcijo "vodnega cikla", cena je tudi 75-95% nižja od čistega korenije . Zato se je v elektronski tehnologiji, toplotni nadzor, sodobni jedrski tehnologiji in vesoljski tehnologiji, merilniki, instrumentov, instrumentov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov, električnih aparatov. Žica z zlitino za volfsten-relium se ujema v termoelement za volframo-rej, ki ima visok termoelektrični potencial in občutljivost ter širok razpon merjenja temperature, hitro hitrost odboja, dobro korozijsko upornost in je dober material za toplotno zaznavanje na področju merjenja temperature .}}}}}}}
1, Mehanske lastnosti molibdene renijeve zlitine
Kot kubična kovina, osredotočena na telo, je čisti molibden pri sobni temperaturi krhek in ima slabo delovanje obdelave, kar omejuje globoko obdelavo in učinkovitost servis kovinskega molibdena do določene mere . dodajanje renijeve molibdene lahko izboljšajo pristojnost molibdena in nato izboljšajo molibsenovo in nato izboljšajo molijsko pristojnost in nato izboljšajo molijsko pristojnost in nato še povečajo, da se še vedno izboljšajo, da se pristojnost za doseganje molibdena še poveča, in nato še izboljšajo, da se bosta še vedno izboljšala, in nato še povečala, da se še vedno izboljšajo pristojnosti molibdena, in nato še izboljšajo molibseno Dodajanje korenije spremeni tudi mehansko deformacijsko vedenje molibdena v procesu vročega in hladnega obdelave iz enojnega zdrsa do dvojnega in zdrsa kombinirano, zavira embritlentnost ogljika in kisika ter izboljša uspešnost materiala ., ki lahko naredijo, da lahko nalivani in zvit izdelki nižji proizvodi, ki imajo spodnji prehodni prehod in znižani proizvodi, ki so v masemih in zmanjšali, da se naliva in valjana proizvoda nižja in valjana proizvoda nižja in valjana proizvoda, ki imajo nižjo prehodno temperaturo in znižani proizvodi, ki so v masemih, ki jih lahko naredijo, in zmanjšajo, da so v materiali, ki jih lahko izlivajo, spuščeni in valjani proizvodi, ki imajo spodnji prehod in zvit proizvodi. ŽELINJE . Ta dodatek khenijevega za izboljšanje lastnosti molibdena se imenuje "renium učinek" .
2, Molibdenska renijeva zlitina toplotne fizikalne lastnosti
Slika 2 prikazuje učinek vsebnosti korenijeve na toplotno prevodnost in koeficient toplotne ekspanzije molibdenske renijeve zlitine ., kot je razvidno iz slike 2, za zlitine molibdena-renija, ki se postopoma povečajo, da se toplotna prevodnost postopoma zmanjša in koeficient toplotne ekspanzije, ki se postopoma zmanjšuje in koeficient postopno narašča Povečanje vsebnosti korenijeve vsebnosti se toplotna prevodnost zlitin molibdena-relije z različnimi sestavki postopoma zmanjšuje pri isti temperaturi . Poleg tega se s povečanjem vsebnosti korenije koeficient toplotne ekspanzije pri isti temperaturi postopoma povečuje .Pojav je naslednji:
Toplotna prevodnost čistega renija je manjša od toplotne prevodnosti čistega molibdena, koeficient toplotne ekspanzije čistega renija
Vpliv vsebnosti renija na toplotno prevodnost in koeficient toplotne ekspanzije zlitin molibdena-renije
Uporaba žice zlitine za volframo-rinium v tehnologiji elektrovakuuma
Glavne zahteve glede zmogljivosti vakuumskih cevi, slikovnih cevi in žarnic vroče žice so:
1: Nizka temperaturna duktilnost, torej dobra žica, ki tvori . obdelane filamente so ranjene, zložene ali zasukane v nitke različnih oblik in velikosti in mora imeti dobro izolacijo med seboj . nizko plastično prehodno temperaturo, dobra enotnost in konsistenco
2: Low temperature annealing ductility is good, that is, two times winding wire formability is good. The filament parts after a wire winding are annealed to fix the shape and size of the parts. Generally, the annealing is carried out within the range of the temperature of a single recrystallization of the wire. Only low temperature annealing of good ductility wire can Izpolnite zahteve sekundarnega navijanja, torej izdelava dvojne vijačnice ali večkratno navijanje in zloženost .
3: High temperature ductility, that is, ductility after secondary recrystallization. To core wire, transport. In the process of tube loading, vibration and impact must be received, and the filament with poor inflammation will be destroyed. The made filament should be used at high temperatures, and most of the filament should exist in a spiral shape during use, and the filament je daljša in ima določeno kakovost . pri uporabi postopka za ohranitev naklona se ne spremeni, visoka temperaturna SAG upor je ključ .
Naše podjetje izdeluje W -3 re Wire, W -5 re Wire, W -20 re Wire, W -25 re Wire lahko izpolni zgornje zahteve .
Uporaba žice zlitine za volframovo-rhenium v materialih z elektronskimi cevmi
Na cev pogosto vplivajo temperaturne spremembe in močna vibracija, naklon spiralne žice pa je enostavno spremeniti, celo trk povzroči električni kratki stik . gola žica je prevlečena s plastjo aluminijevega oksida v prahu, da izboljša moč in povečajo, da se temperatura nižva Spiralna trk s filamentom .
Žica zlitine za volfsten-rhenium, ki se uporablja v filamentu za elektronsko cev, ima širok razpon komponent . filament z dobrimi zmogljivostmi proti-Sag je na splošno dopirana w -3 relfsten-rhenium zlitina žica . returity je na splošno uporabljena kot W W -25 re Tungsten Rhenium Alloy Wire . Test vijuganja žice in življenjske dobe elektronske cevi, narejene iz žice zlitine za volfsten-Rhenium, se izvedejo ., pri čemer se rezultati prikazajo v primerjavi z 2000 stopnjah, ko se na 2000 stopnjah in 2500 stopnje, ko se junira na 2000 stopinj, ko se junira na 2000 stopnje Poradi žice se poveča, kar kaže, da se plastičnost zlitine z visoko vsebnostjo renije zmanjša, zmogljivost navijanja žice je slaba, vendar se življenjska doba filamenta poveča .
Satelitske cevi zahtevajo dolgo življenjsko dobo, več deset tisoč ali celo sto tisoč ur, velika zanesljivost in upornost vibracij . Pri zagonu umetnega zemeljskega satelita je bila elektronska cev podvržena {{1} g gravitacijskim pospeševalnim vibracijam {{2} doped tungened tungine {{2} doped tungine tUngud tungine {{2} doped tungine tungened {{2} doped tungine tUNGSTEN TUNUN TUNUN TUNUN TUNUN TUNUN TUNUN TUNUNDEN Kot surovina, dodajanje visoke vsebinske dopant in kobalt . po pranju z hidrofluorovo kislino je bilo pomešano z raztopino amonijevega rhenata, nato Žica izdeluje rotacijsko kovanje in risanje . Ta vrsta zlitine lahko ustreza zahtevam satelitske dolge življenjske filamente .
Elektronska cev, ki jo uporablja zemeljska sprejemna postaja umetnega zemeljskega satelita, zahteva visoko mehansko trdnost in ne bo pretrgala elektronske cevi pri prejemanju resonance iste frekvence; Upogibanje 90 stopinjskega kota ni krhko razdeljeno, se zlomi in razpoka; Hitrost izhlapevanja nitke je nizka, da prepreči, da bi bila stena cevi iz črnine
Ogrevalna filament elektronske pištole za pospeševalno cev v stroju za zdravljenje in industrijskega zaznavanja napak uporabljajo žico zlitine za volfsten-rhenium, da zagotovi zahteve rezancev dolge življenjske dobe in drugih življenjskih zahtev .
Zložljiva filament visokonapetostnega usmernika je narejena iz žice zlitine za volfsten-rhenium, ki ni krhka . cepljenje, lomljenje in pokanje, konsistenca električnih parametrov cevi za usmerjevanje pa je boljša .